Effect of Annealing on Structural and Surface Properties of Nanostructured ZnO Thin Films

T. Shiyani, U. D. Khachar, R. Mansuriya, P. Solanki, R. Doshi, P. Vachhani, J. H. Markna, D. G. Kuberkar

Abstract


ZnO thin films with different grain size were grown on amorphous quartz substrate using spin coating method. We have reported the effect of annealing temperatures on the structural and surface properties of ZnO thin films. The surface properties were characterized by AFM. From XRD analysis, it can be seen that, the FWHM decreases with an increase in annealing temperature from 500 to 575ºC which is reflected in the increase in the particle size with annealing temperature. The grains are well developed in nature with the size ranging between 100 and 200 nm and the height of the grains range between 25 and 55 nm. The absorption spectrum in the UV-visible range of ZnO film was taken to confirm the diameter of nanoparticle. The value of the average diameter (D) of ZnO particle in the CSD grown film is estimated to be ~10 nm, which is in the range of the particle size obtain from XRD.

Keywords


ZnO, thin film, microstructure, annealing

Full Text:

PDF

References


Zhen hua Chen, Trans Nonferrous Met Soc. 2007; 6(17): 1379–1384p.

Poole Charles P, Owens Frank J. Introduction to Nanotechnology; John Wiley & Sons Publication, 2003.

Pradeep T, Nano: The Essentials; TMH Publishing Company Limited: India, 2007.

Kulkarni SK, Nanotechnology: Principles and Practices; Springer: India, 2011.

Nabok Alexei, Organic and Inorganic Nanostructures; Artech House Publishing Company, 2005.

Goswami A, Thin Film Fundamentals; New Age Publishing Company: India, 2008.

Natsume Y, Sakata H, Thin Solid Films, 2000; 372: 30–36p.

Zhao JL, et al. J Cryst Growth. 2005; 276: 507–512p.

Cheng XL, et al. Sensors Actuator B. 2004; 102: 248–252p.

Zhaoa Jun-Liang, Lia Xiao-Min, Biana Ji-Ming, et al. J Cryst Growth. 2005; 276: 507–512p.

Shin Paik Kyun, Aya Yoichiro, Ikegami Tomoaki, et al. Thin Solid Films. 2008; 12: 3767–3771p.

Shalimov A, Paszkowicz W, Grasza K, et al. J Phys. Stat. 2007; 244(5): 1573–1577p.


Refbacks